IntroductionFlow injection polymer analysis (FIPA) is a fast, precise and accurate analytical tool for routine process and quality control measurements. This technique provides quick and easy simultaneous measurements of the weight average molecular weight (MW), the weight average intrinsic viscosity (IVW), the weight average hydrodynamic size (RH) and the composition, %Polymer for liquid process/production/research samples. In FIPA, concentration can be calculated so the solutions need to be prepared only at an approximate concentration. In this application communication we show how this technique can be used for a solvent like HFIP, which is very expensive and hazardous for the user, but is an excellent solvent to dissolve polyesters like (PET, PBT) and polyamides (nylon 6 and nylon 6,6). Due to the short analysis time it is possible to make significant savings in HFIP costs and give fast feedback to the plant about the results obtained.ExperimentalCommercially available PET samples having a nominal Mw were used. The samples were injected sequentially and analysed for their molecular weights and intrinsic viscosity. In this case the samples were prepared to a known concentration, therefore the software was not used to calculate the sample concentration but to verify that 100% of the sample eluted through the FIPA column. All the concentrations were prepared to about 2.4 mg/mL.The FIPA system used a Viscotek GPCmax equipped with the standard degasser, isocratic pump and autosampler. The column, a ViscoGEL FIPA column was placed in the isothermal compartment of the Viscotek TDA system which was kept at a temperature of 35 °C. The Viscotek Triple Detector Array (TDA) included the RI detector, the light scattering detector and the differential viscometer detector all in the isothermal compartment of the TDA. The solvent used was hexa fluoro isopropanol (HFIP) with 0.1% KF3Ac.ResultsThe software calculated a recovery of 100% (+/- 1%) which meant that all the concentration were prepared to the calculated concentration. It also verified that the entire polymer was dissolved in the solution. The +/- 1% deviation is from the noise in the measured concentration.Figure 1: a) FIPAgram of PBT 44K sample shown as an example.When the repeatability of this measurement is examined we observed that both viscosity and molecular weight measurements can be measured very precisely. Figure 1 shows a typical FIPAgram. In this case the PBT 44K was measured. It should be noted that the volume needed is 5 mL for this chromatogram. In table 1, the injections results are presented. The injection time is also presented showing that injections were made about 10 minute apart.Table 1: Weight average molecular weight, weight average intrinsic viscosity and size for various polymers in HFIP.SampleDate and TimeMW (g/mol)IVW (dL/g)RH (nm)PET 49K205/07/2009 10:2547,4670.8058.455PET 49K205/07/2009 10:3648,1270.8068.495PET 49K205/07/2009 10:4748,1650.8008.477PET 49K205/07/2009 10:5848,6020.8028.509PET 49K205/07/2009 11:0948,8950.8018.524PET 8K105/07/2009 11:415,3940.1602.389PET 8K105/07/2009 11:525,5100.1722.466PET 39K05/07/2009 12:0338,8550.7487.716PET 39K05/07/2009 12:1438,8810.7487.718PET 63K505/07/2009 12:2577,6881.17911.315PET 63K505/07/2009 12:3677,4201.17411.284PBT 29K05/07/2009 13:0929,4490.8307.285PBT 29K05/07/2009 13:2029,4880.8327.295PBT 37K05/07/2009 13:3042,3361.0598.918PBT 37K05/07/2009 13:4142,4841.0658.943PBT 44K05/07/2009 13:5251,1191.2099.925PBT 44K05/07/2009 14:0351,2541.2109.935PBT 55K05/07/2009 14:1474,5711.60812.377PBT 55K05/07/2009 14:2575,4591.60512.419Nylon 605/07/2009 14:3685,8472.50815.044Nylon 605/07/2009 14:4784,8212.51114.990Table 2: Weight average molecular weight, weight average intrinsic viscosity standard deviation for 5 repeat FIPA measurements.SampleDate and TimeMW (g/mol)IVW (dL/g)RH (nm)PET 49K205/07/2009 10:2547,4670.8058.455PET 49K205/07/2009 10:3648,1270.8068.495PET 49K205/07/2009 10:4748,1650.8008.477PET 49K205/07/2009 10:5848,6020.8028.509PET 49K205/07/2009 11:0948,8950.8018.524Average48,2510.8038.492Standard Deviation5420.0030.027%RSD1.10.30.3The repeatability is presented in table 2. With 5 consecutive measurements of poly ethylene terephtalate (PET), the molecular weight had a relative standard deviation of only 1.1%. Both the intrinsic viscosity and radius had a relative standard deviation of 0.3%.ConclusionFIPA is a fast and accurate way of measuring molecular weight, intrinsic viscosity and hydrodynamic radius. Concentration does not have to be known exactly since it can be calculated through the OmniSEC software. This also means that polymer % can be calculated for each sample. The ratio of IV and MW can give information about branching. For applications with hazardous solvent like HFIP, FIPA is a fast technique that can limit solvent costs and exposure to this solvent. FIPA can easily replace difficult Ubbelohde measurements and since the molecular weight is measured directly via the light scattering detector it avoids calculation via the Mark-Houwink equation which is only valid for molecules of the same structure. The GPCmax solvent delivery system (degasser and pump) includes an auto sampler that can inject from 2 ml vials when only small amounts of sample are available. In this set-up with a flow of 0.5 ml/min it is possible to measure 6 samples in 1 hour which is about 6 times faster than a regular GPC measurement in HFIP.