Polycaprolactone (PCL) is a synthetic polymer that has recently received increasing attention thanks to its biodegradability.  Its most common use is in the manufacture of polyurethanes or as a plasticizer for other polymers such as PVC.  It is also often used in molding and prototyping thanks to its low melting temperature and is used as a feedstock in some additive manufacturing (3D printing) systems.  Finally, it is also used in some drug delivery applications as a control release mechanism, in the same way as polylactic acid (PLA) or polylactic-co-glycolic acid (PLGA).  A potential advantage over PLA and PLGA is that PCL has a slower degradation rate and therefore may allow for slower drug release.

As with all polymers, PCL’s molecular properties (e.g. molecular weight) will strongly affect its bulk properties such as strength, toughness, and melt-flow.  Being biodegradable, PCL is at a high risk of degradation during processes such as extrusion for molding, particularly at high temperatures.  Some mechanisms have been described in the literature to reduce this.  For instance, extrusion in the presence of carbon dioxide (CO2) can reduce the melt flow viscosity of PCL by acting as a ‘molecular lubricant’.  Decreasing the viscosity of the polymer reduces the temperature at which extrusion can be performed and could thereby protect the polymer from degradation during the process [1].

In this application note, a commercially available sample of PCL was extruded alone and in the presence of CO2­.  Multi-detector GPC measurements were made of the virgin sample before and after extrusion, while rotational rheometry was used to study the polymer’s melt viscosity.

ログイン

初めての方

会員登録いただくと、以下のような会員様限定コンテンツを無料でご覧いただけます。

  • 録画版ウェブセミナー、プレゼン資料、動画
  • アプリケーションノート、技術資料、記事、ホワイトペーパー、ソフトウェアダウンロード

加えて、以下の情報が定期的に届くメールニュースにも任意でご登録いただけます。

  • 最新のマルバーン・パナリティカル製品情報、技術情報、分析について学べるセミナー・ウェブセミナー・イベント情報