ASTM C114-15 and ISO 29581-2 compliance for cement fused beads

With the latest innovations in X-ray tube and detector technology in the Epsilon 4, this system, in combination with the Eagon 2 fully automatic fusion system, complies with the latest cement testing methods of both ASTM C114-15 and ISO 29581-2.

The data presented in this datasheet clearly demonstrate the compliance of the Epsilon 4 XRF spectrometer, in combination with the Eagon 2 automatic fusion machine, with both the ASTM C114- 15 and ISO 29581-2:2010 cement test methods for the quantitative analysis of SiO2, Al2O3, Fe2O3, CaO, MgO, SO3, K2O, Na2O, TiO2, P2O5, ZnO and Mn2O3 in cement, prepared as fused beads.

Introduction

X-ray fluorescence spectroscopy (XRF) has an important and well-established analytical role within the cement industry. It is used extensively for production and quality control for the elemental analysis of raw materials, alternative fuels and finished products. Low-power benchtop energy dispersive XRF instruments (EDXRF) were never considered a reliable analytical tool in this environment, since they could not satisfy the relevant international ASTM and ISO cement test methods. With the latest innovations in X-ray tube and detector technology in the Epsilon 4, this has changed. This system, in combination with the Claisse Eagon 2 fully automatic fusion system, complies with the latest cement testing methods of both ASTM C114-15 and ISO 29581-2, in 10 minutes.

ASTM C114-15 gives recommendations for the maximum deviation of analytical results for a selection of important compounds in cement. In brief, the norm suggests that the analyses must be made in duplicate on different days. Two criteria apply, one for the differences between duplicates measured on different days and one for the differences between the averages of the duplicates and the certified values.

ISO 29581-2 specifies the limits for accuracy and repeatability of the analysis of compounds in cement samples. The limits are specified in two performance levels: ‘normal’ and ‘expert’.

Instrumentation and measurement conditions

A PANalytical Epsilon 4 spectrometer was used to carry out the measurements. The system is equipped with a 15W, 50 kV silver anode X-ray tube, 6 software selectable filters, a helium purge facility, a high- resolution SDDUltra silicon drift detector, a spinner and a 10-position removable sample changer. The applied measurement conditions are shown in Table 1, with a measuring time of 10 minutes per sample. Net intensities were derived from the acquired spectra by deconvolution, except for Na, which was obtained by region of interest (ROI).

A Claisse Eagon 2 fully automatic fusion machine was used to prepare the fused beads. The innovative 2-position design combines the advantages of gas burner and muffle furnace technologies in a system that does not require hazardous and costly gas supplies, cooling water or compressed air. The Eagon 2 only requires a simple electrical connection. Its fully automatic, push-button operation ensures a high level of repeatability and ‘cold to cold’ operation for safety at all times.

Epsilon 4

The Epsilon 4 is a fully integrated energy dispersive XRF analyzer consisting of a spectrometer, 10-position sample changer with integrated spinner and mature software. Powered by the latest advances in excitation and detection technology  the Epsilon 4 is a star performer in the benchtop instrument class. A high-resolution SDDUltra silicon drift detector, a well-designed optical path and a wide range of excitation capabilities contribute to the Epsilon 4’s uniqueness

Table 1. Epsilon 4 measurement conditions 

table1.PNG

Sample preparation

Twenty-four certified reference materials (CRMs) were prepared as fused beads and used to set up calibrations for all of the specified elements. The CRMs included NIST (1880b, 1881a, 1884b, 1885a, 1886a, 1887a, 1888b and 1889a), JCA (XRF 1 – 15)

and BCS 354. Prior to bead preparation, the samples were dried overnight in an oven at 105 ºC and ignited in a muffle  furnace at 950 ºC for at least one hour. The flux, FX-65 (66 % Li2B4O7 / 34 % LiBO2), was kept dry and stored in an oven at 105 ºC. Fused beads were prepared using a 5:1 flux sample ratio at a fusion temperature of 1050 ºC in an Eagon 2. In accordance to the test methods, the duplicates were prepared on different days.

Calibration setup

Calibrations were set up using 24 interna- tional standards, prepared in duplicates (NIST 1880b, 1881a, 1884b, 1885a, 1886a, 1887a, 1888b, 1889a, JCA-XRF 1 to 15 and BCS 354). The FP model was used as matrix correction model. Figures 1 and 2 show calibration graphs of Fe2O3 and Na2O in cement CRMs prepared as fused beads, respectively.

Figure 1. Calibration graph of Fe2O3 in cement CRMs, prepared as fused beads (red dots represent the excluded standards, according to the test methods)

figure1.PNG

Figure 2. Calibration graph of Na2O in cement CRMs, prepared as fused beads (red dots represent the excluded standards, according to the test methods

figure2.PNG

Procedure

Eight international NIST Portland SRM ce- ment reference materials were selected to produce two sets of fused bead samples to demonstrate instrument and sample preparation performance. These sets were prepared and measured on different days. The difference between the measurements on both days is a measure of the overall precision of the method, while the differ- ence of the average of the values from both days to the certified values is a mea- sure of the overall accuracy of the method.

Compliance with ASTM C114-15 

Table 2 shows the summary of all eight validation samples, the maximum measured concentration difference between duplicate samples, the maximum measured concentration difference between the average values of the duplicates and certified concentrations, and the relevant allowed limits set by the ASTM C114-15 test method. The measured concentration differences for all the compounds in all eight validation samples were smaller than the permitted differences of the norm. This means

that the Epsilon 4 meets ASTM C114-15 requirements for SiO2, Al2O3, Fe2O3, CaO, MgO, SO3, P2O5, K2O, Na2O, TiO2, Mn2O3 and ZnO in cement samples prepared as fused beads. The results of the duplicate test are illustrated graphically in Figure 3 for SiO2 and the results of the accuracy test are illustrated graphically in Figure 4.

Table 2. Summary of the accuracy test obtained for eight NIST validation samples compared to ASTM C114-15 limits 

table2.PNG

Figure 3. Summary of the duplicate test obtained for eight NIST validation samples compared to ASTM C114-15 limit for SiO2 

figure3.PNG

Figure 4. Summary of the accuracy test obtained for eight NIST validation samples compared to ASTM C114-15 limit for SiO2 

figure4.PNG

Compliance with ISO 29581-2:2010

In accordance to ISO 29581-2, NIST 1888b and JCA XRF 13 were measured as unknowns and those standards were not included in the calibration graphs. The measured concentrations were compared to the certified values. Table 3 presents the accuracy results obtained for these two validation samples by showing the difference between the measured and the certified values, and the maximum difference allowed by the ISO norm. The repeatability of the method was tested by measuring NIST 1881a validation samples  for ten times over a period of six days.  The results are shown in Table 4 and graphically illustrated for SiO2 and Al2O3 in Figures 5 and 6, respectively. Both ‘normal’ and ‘expert’ performance levels are shown in the graphs for comparison.

Figure 5. Repeatability over 6 days of SiO2 in NIST SRM 1881a according to ISO 29581-2 

figure5.PNG

Figure 6. Repeatability over 6 days of Al2O3 in NIST SRM 1881a according to ISO 29581-2 

figure6.PNG

Table 3. Summary of the accuracy test obtained for two validation samples according to ISO 29581-2 limits 

table3.PNG

Table 4. Summary of the repeatability test obtained for NIST SRM 1881a according to ISO 29581-2 limits 

table4.PNG

Conclusion

The data presented in this application note clearly demonstrate the compliance of the Epsilon 4 XRF spectrometer, in combination with the Eagon 2 automatic fusion machine, with both the ASTM C114-15 and ISO 29581-2:2010 cement test methods. Quantitative analysis of SiO2, Al2O3, Fe2O3, CaO, MgO, SO3, K2O, Na2O, TiO2, P2O5, ZnO, SrO and MnO3 in cement, prepared as fused beads was performed in 10 minutes.